HF/FHF Polyimide-Fluorine-46 Composite Film

 

Product No.:MAF03 Q-MANTIC ®  Polyimide-Fluorine-46 Composite Film (HF,FHF) is made by dipping and coating F-46 emulsion on polyimide film then solidified at high temperature. Self-melt and the ability to seal under high temperature is these films’ special properties. It also has the excellent characters in electric insulation, resistance to high temperature, radiation and corrosion as well as self-melting and seal under high temperature etc. MAF03 is close to Kapton® Type FN. It is recommended for applications that require a heat-bondable film, or moisture and chemical resistance beyond the capabilities of general purpose polyimide film. H or V type Polyimide film doesn’t melt or burn and has excellent chemical resistance; there are no know organic solvents for the film. Application includes tubing, heater circuits, heat-sealable bags and automotive diaphragms.
 

Product Detail

Remarks

■ FH Film: Single-side, FHF Film: Double-side ■ Width: 10mm-550mm ■ Base film thickness: 0.025-0.075mm ■ F-46 layers thickness: 0.003-0.02mm

Features

■ High Temperature electrical insulation ■ Cut-through resistant ■ High bond strength ■ High dielectric strength

Characteristic

Similar as

120FN616

200FN919

300FN929

500FN131

150FN019

200FN011

300FN021

Thickness  µm(inch)

31(0.012)

50(0.002)

75(0.003)

125(0.005)

38(0.0015)

50(0.0002)

75(0.0003)

Structure (µm) FEP

3.0

7.5

12.5

12.5

12.5

15.0

15

PI

25.0

35.0

50.0

100.0

25.0

35.0

60.0

FEP

3.0

7.5

12.5

12.5

0

0

0

Thickness Tolerance (%) ±10
Tensile Strength (MPa) ≥ MD

130

 100

80

80

140

100

110

TD

110

 80

75

70

110

80

90

Elongation at rupture (%) ≥

50

 50

50

50

50

60

60

Breakdown Strength (MV/m) ≥ Average

150

 120

120

110

150

120

110

Individual

120

 110

110

100

120

100

100

Peel Strength (N/25mm) ≥ F-F

6.0

 6.5

6.7

6.7

N/A

N/A

N/A

F-H

N/A

 N/A

N/A

N/A

6.0

6.0

6.0

Surface Resistivity  200+/-5 ºC (392F) (Ω)≥

1.0 ×1013

Volume Resistivity  200+/-5 ºC (392F) (Ω·m)≥

1.0 ×1010

Dielectric constant  (50Hz)

3.5±0.4

Loss tangent  (50Hz)≤

4.0 ×10-3

Application

■ Turn insulation in motors and generators ■ Electrical insulation of flexible heater ■ Wire and cable insulation

Packing

■ Min. slitting width: 6mm ■ Core ID: 3”/ 6” ■ Winding: Pad type/Step-pac Type/Universal Type ■ Storage: Keep in room temperature. Remove package before use. Unused parts are wrapped in original packaging to avoid moisture absorption. It is recommended to be used up in 6 months.